Rincian Produk
Tempat asal: Cina
Nama merek: KAIXIN
Sertifikasi: ISO9001:2015
Nomor model: KX-Paduan IN718
Ketentuan Pembayaran & Pengiriman
Kuantitas min Order: 200kg
Harga: To negotiate
Kemasan rincian: Kotak Kayu, ukuran sesuai permintaan tamu
Waktu pengiriman: 45 ~ 60 hari
Syarat-syarat pembayaran: T/T, L/C
Menyediakan kemampuan: 50~80 TON per BULAN
Membentuk: |
Kawat, Strip, Batang, Pipa, Piring |
Tipe Paduan: |
Superalloy Cacat Berbasis Nikel |
Bahan baku: |
NI50-55%,CR17-21%,NB4.75-5.5%,MO2.8-3.3% |
Standar eksekutif: |
ASTM |
Negara Pengiriman: |
Sosoloid |
Aplikasi: |
Suku cadang untuk mesin pesawat, industri energi nuklir, dan aplikasi perminyakan |
Fitur: |
ketahanan lelah, ketahanan radiasi, ketahanan oksidasi, ketahanan korosi |
ukuran: |
Dapat dinegosiasikan |
Membentuk: |
Kawat, Strip, Batang, Pipa, Piring |
Tipe Paduan: |
Superalloy Cacat Berbasis Nikel |
Bahan baku: |
NI50-55%,CR17-21%,NB4.75-5.5%,MO2.8-3.3% |
Standar eksekutif: |
ASTM |
Negara Pengiriman: |
Sosoloid |
Aplikasi: |
Suku cadang untuk mesin pesawat, industri energi nuklir, dan aplikasi perminyakan |
Fitur: |
ketahanan lelah, ketahanan radiasi, ketahanan oksidasi, ketahanan korosi |
ukuran: |
Dapat dinegosiasikan |
KX UNS N07718 Nickel Alloy Wire Round Bar Tube Steel Sheet Light Rod on Inconel Alloy
Deskripsi Produk dan Aplikasi
UNS N07718 adalah superalloy deformasi pengerasan presipitasi dasar Ni-Cr-Fe dengan kisaran suhu operasi jangka panjang -253℃~650℃ dan suhu operasi jangka pendek 800℃.Paduan ini memiliki kekuatan tinggi di bawah 650 ℃ dan memiliki ketahanan lelah yang baik, ketahanan radiasi, ketahanan oksidasi dan ketahanan korosi, serta kemampuan proses yang baik, kemampuan las dan stabilitas struktural jangka panjang.Cocok untuk pembuatan cakram turbin, cincin, bilah, poros, pengencang dan komponen elastis, bagian struktural pelat, selubung dan sebagainya dalam industri penerbangan, kedirgantaraan, energi nuklir, dan petrokimia.Produk utama adalah batang canai panas dan tempa, batang tarik dingin, pelat dan strip, kawat, pipa, cincin dan tempa dll. Komposisi paduan dibagi menjadi kualitas biasa dan kualitas tinggi, kualitas tinggi.Kontrol kandungan karbon, niobium, sulfur dan gas UNS N07718 lebih ketat, terutama digunakan untuk pembuatan semua jenis bagian yang berputar. Teknologi pemrosesan dapat dibagi menjadi standar, kekuatan tinggi dan penuaan langsung.Kekuatan tinggi dan proses penuaan langsung digunakan untuk kualitas tinggiUNS N07718tempa paduan.Suhu deformasi panas menurun berturut-turut, ukuran butir rata-rata tempa memurnikan berturut-turut dan kekuatan meningkat berturut-turut, yang dapat memenuhi persyaratan aplikasi berbagai bagian berputar di mesin aero.
Kinerja Proses dan Persyaratan
Tungku Induksi Vakum (VIM) dan Tungku Peleburan Elektroslag (ESR)
| Paduan | % | Ni | Kr | Fe | Mo | Nb | Bersama | C | M N | Ya | S | Cu | Al | Ti |
| UNS N07718 | Min | 50 | 17 | Rem | 2.8 | 4.75 | 0,20 | 0,65 | ||||||
| Maks | 55 | 21 | 3.3 | 5.50 | 1.0 | 0,08 | 0,35 | 0,35 | 0,015 | 0,30 | 0,80 | 1.15 |
| Kepadatan | 8,24/cm3 |
| Titik lebur | 1260-1320℃ |
| Properti Magnetik | Nol |
| Temperatur Peleburan | 1260 ℃ ~ 1320 ℃ |
| Variasi dan Spesifikasi | Perawatan panas | Properti Tarik | Kekerasan | Daya tahan | |||||
| MPa | MPa | % | MPa | r/h | % | ||||
|
Plat/Lembaran/Strip |
--- | Anil | ≤895 | ≤485 | ≥40 | HRB≤ 94 | --- | --- | --- |
| Plat/Lembaran/Strip | ≤ 0,25 | Solusi Padat | ≤965 | ≤550 | MV | HRB≤ 102 | --- | --- | --- |
| Plat/Lembaran/Strip | ＞0,25~4,75 | ≤965 | ≤550 | ≥30 | HRB≤ 102 | --- | --- | --- | |
| Plat/Lembaran/Strip | ＞4,75~25 | ≤1035 | ≤725 | ≥30 | HRC≤ 25 | --- | --- | --- | |
| Plat/Lembaran/Strip | ≤ 0,25 |
Standar Perawatan panas |
≥1240 | ≥1035 | MV | HRC≤ 36 | --- | --- | --- |
| Plat/Lembaran/Strip | ＞0,25~25 | ≥1240 | ≥1035 | ≥12 | HRC≤ 36 | --- | --- | --- | |
| Plat/Lembaran/Strip | ≤ 0,38 | ≥965 | ≥795 | ≥5 | --- | 655 | ≥23 | --- | |
| Plat/Lembaran/Strip | ＞0,38~0,62 | ≥965 | ≥795 | ≥5 | --- | 655 | ≥23 | 4 | |
| Plat/Lembaran/Strip | ＞0,62~25 | ≥1000 | ≥825 | ≥5 | --- | 690 | ≥23 | 4 | |
| Nomor Standar | Variasi | Perawatan panas | ℃ | Properti Tarik | ||
| MPa | MPa | % | ||||
| Q/3B 4052 | Pembuluh kapiler | Solusi Padat | 20 | ≤ 1070 | ≤ 655 | ≥ 30 |
| Perlakuan Panas Standar | 20 | ≥ 1275 | ≥ 1035 | ≥ 12 | ||
| Keterangan: Spesimen tarik seluruh tabung digunakan | ||||||
| Nomor Standar | Variasi | Perawatan panas | ℃ | Properti Tarik | Kekerasan | Daya tahan | |||||
| MPa | MPa | % | % | MPa | r/h | % | |||||
| GJB 2611A | Batang Ditarik Dingin |
Standar |
20 | ≥ 1270 | ≥ 1030 | ≥ 12 | ≥ 15 | HBW≥ 345 | --- | --- | --- |
| 650 | ≥ 1000 | ≥ 860 | ≥ 12 | ≥ 18 | --- | 690 | ≥ 23 | ≥ 4 | |||
| GJB 3527 | Kawat Ditarik Dingin untuk Pegas | 20 | ≥ 1270 | ≥ 1035 | ≥ 12 | -- | HBC≥ 32 | --- | --- | --- | |
Institusi Perlakuan Panas Produk
Kabel
955℃±10℃x1h/AC+720℃士10℃x8h/FC(50℃士10℃/h)→620℃±5℃×(7`8)h/ AC,HRC≥32;
Batang dan Tempa
(950~980)℃士10℃x1h/AC+720℃±5℃x8h/FC(50℃士10℃/h)→620℃±5℃ x8h/AC,HB≥346;
Bagian Plat dan Pengelasan
Institusi I:(940~960)℃/AC+(710~730)℃x(8~8.5)h/FC(50℃±10℃/h)→(615~620)℃x(8~8.5)h/ AC, Larutan Padat Waktu penahanan:(d)≤3mm,(25~30)min;(d)3mm~5mm,(30~35)min;
Tabung
955 ℃ 士 10 ℃ x30min / AC (atau berpendingin udara) + 720 ℃ ± 10 ℃ x8h / FC (50 ℃ ± 10 ℃ / jam) → 620 ℃ ± 10 ℃, Jadikan total waktu penahanan tidak kurang dari 18 jam, berpendingin udara atau pendinginan udara paksa
Perawatan penuaan langsung untuk tempa disk: 720 ℃ 士 10 ℃ x8h / FC (50 ℃ ± 10 ℃ / jam) → 620 ℃ ± 10 ℃ x8h / AC
Kustomisasi Profesional
| CkunoWkemarahan | ¢0,3~¢18mm (Pengiriman dalam gulungan atau baki) |
| Hatau-RollingWkemarahan | ¢5.5~¢20mm(Pengiriman dalam bentuk gulungan) |
| Sperjalanan | ketebalan 0,1 ~ 4,5 * lebar 6 ~ 350mm (Pasokan dalam gulungan atau strip lurus) |
| Smooth DitempaRod pada aLmakan |
¢60~350mm,L800-2500mm
|
| Hot-rolledBperlengkapan | ¢20~80mm,L1000-5000mm |
| DinginDmentah danBperlengkapan | ¢2.5~18mm,L1000-8000mm |
| Stanpa cacatTube | ¢1~275mm, ketebalan dinding 0,2~30, L1000-8000mm |